Corrosion Rate Analysis of JIS G-3141 Steel for Automotive Inner Wheel House Production with Weight Loss Method
Abstract
The growth of car sales and production has decreased since 2020, this is due to corrosion of automotive steel plates in the form of low carbon steel stored in warehouses. The purpose of this study was to obtain the value of the corrosion rate and its effect on mechanical properties and changes in the composition of carbon values. Low carbon steel plates commonly used by automotives where the material is low carbon steel JIS G-3141, with its elemental content of C 0.12%, Mn 0.5%, P 0.04% and S 0.045% with tensile mechanical properties. strength 270 N/mm2, elongation 37%. The purpose of this study was to obtain the value of the corrosion rate and its effect on mechanical properties and changes in the composition of carbon values. Low carbon steel plates commonly used by automotives where the material is low carbon steel JIS G-3141, with its elemental content of C 0.12%, Mn 0.5%, P 0.04% and S 0.045% with tensile mechanical properties. strength 270 N/mm2, elongation 37%.
Full Text:
PDFReferences
Ali, N., & Fulazzaky, M. A. (2020). The empirical prediction of weight change and corrosion rate of low-carbon steel.Heliyon,6(9),e05050.https://doi.org/10.1016/j.heliyon.2020.e 05050
Anon. (1985). Standard Practice for Laboratory Immersion Corrosion Testing of Metals. ASTM Special Technical Publication, i(Reapproved), 534–544.
ASM Metals Handbook. (1990-1, 2005-2), “Vol 01 : Properties and Selection Irons, Steels, and High-Performance Alloys”, ASM International.
Di, A., & Jember, K. (2012). Evaluasi Korosi Baja Karbon Rendah Astm A36 Pada Lingkungan Atmosferik Di Kabupaten Jember Sumarji 1. 5, 44–51.
Fontana, M.G.(1987). Corrosion Enginnering (Third Edition). Singapore:McGrawHillBook Company.
Gapsari, Femiana. 2013. Pengantar Korosi. Malang: UBMedia.
Jones, D. A. (1996). Principles and prevention of corrosion, Prentice-Hall International, NJ, USA (p. Prentice- Hall International, NJ, USA).
Mulyanto, B., & Khaerudini, D. S. (2020). Investigasi simulasi numeris dan eksperimen proses springback berbentuk cup silider pada lembaran baja karbon Jis-G3141. Dinamika TeknikMesin, 10(1),60 https://doi.org/10.29303/dtm.v10i1.326
Abu-Dalo, M. A., Othman, A. A., & Al-Rawashdeh, N. A. F. (2012). Exudate gum from acacia trees agreen corrosion inhibitor for mild steel in acidic media. International Journal of Electrochemical Science, 7(10), 9303–9324.
Ali, N., & Fulazzaky, M. A. (2020). The empirical prediction of weight change and corrosion rate of low-carbon steel. Heliyon,6(9),e05050. https://doi.org/10.1016/j.heliyon.2020.e 05
Arwati, I. G. A. (2017). Aluminum Corrosion Analysis for Environmental Acid Chloride Solution. 1(5), 65–69.
Onyeachu, I. B., & Solomon, M. M. (2020). Benzotriazole derivative as an effective corrosion inhibitor for low carbon steel in 1 M HCl and 1 M HCl + 3.5 wt% NaCl solutions. Journal of Molecular Liquids, 313, 113536. https://doi.org/10.1016/j.molliq.2020.11 3536
Ramadani, A. (2017). Analisis Perbedaan Laju Korosi Material Jari-Jari Sepeda Motor (Spokes) Pada Berbagai Media Air Yang Berkonsentrasi Asam Di Daerah
Deni ShidIq Khaerudini, https://www.sciencedirect.com/science/article/abs/pii/S0254058419311095 - !SagirAlva .2020. Optimization strategy of Ag/AgCl thin film electrodes approached by chlorination process for electrochemical response materials , Materials Chemistry andPhysicsol.240.
DOI: http://dx.doi.org/10.48181/wcej.v6i1.14377
Refbacks
- There are currently no refbacks.
Copyright (c) 2022 World Chemical Engineering Journal
WCEJ (e-ISSN: 2443-2261) is published by Chemical Engineering Department, University of Sultan Ageng Tirtayasa (UNTIRTA).
This Journal has been indexed by:
Google Scholar
Open Academic Journal Index
JIFACTOR (Journal Impact Factor)
Cite Factor
General Impact Factor (on Progress)
This work is licensed under a Creative Commons Attribution-ShareAlike 4.0 International License.