Studi Karakterisasi Sintesis Nano Partikel ZnO Menggunakan Metode Kopresipitasi dengan Varian Konsentrasi Dopping Cu

Radityo Rangkuti, Heru Harsono, Muhammad Ghufron

Abstract


Syntesis of ZnO nano particles using co-precipitation methode with variation of cu-doped consentrate has been done. This research devided by two part, the first part is syntesis process, and the second part is characterization process. The first step of synthesis process is by measuring Zn assetate and CuS mass to get variation of Cu –Doped consentration which is 0%, 2%, 4%, 6%, and 8%, then dissolved it with 150 ml HCl 0.5 M. The next step is by droping on solution slowly until pH 10, then the solution stired on a hotplate for 3 hours with 60⁰ C temprature. Next, the synthesis proceed is done after following this procees which is preticipation, purification, and drying with 150⁰ C. Characterization proses has been done by using SEM-EDX and XRD. Ressult by using XRD ZnO phase found in 0%, 4%, 6%, and 8% Cu-doped. The smallest average of diameter crystallin acquaired from a sampel without Cu-doped which is 29 nm, and the largest is acquaired from a sampel with 8% Cu-doped which is 37 nm. SEM-EDX result shown particles morfology and the persentage of mass and atom. As it result can be concluded The persentage of mass and atom Cu greater along the consentration

Keywords


Zinc Oxide, nano particles , coprecipitation, Cu-Doped

Full Text:

PDF

References


Anonymous. (2007). Nano Partikel. Institute Teknologi Bandung. Retrieved from http://digilib.itb.ac.id/files/disk1/552/jbptitbpp-gdl-dianperdan-27551-2-2007ta-1.pdf

Anonymous. (2010). BAB II. Retrieved from http://eprints.undip.ac.id/47843/6/BAB_II.pdf

Beutol, J. (2000). Medical Imagine. Production (Vol. 1). Washington: Spie Press. https://doi.org/10.1088/0031-9120/5/6/113

Harsono, H., Wardana, I. N. G., Sonief, A. A., & Darminto. (2015). Crystallography, Impurities and Magnetic Properties of Mn-Doped ZnO Nanoparticles Prepared by Coprecipitation Method. Journal of Nano Research, 35, 67–76. https://doi.org/10.4028/www.scientific.net/JNanoR.35.67

Jacobsson, T. J. (2009). Synthesis and characterisation of ZnO An experimental investigation of some of their size dependent quantum effects. Materials Chemistry, 1–73.

Kim, E., Iroaga, E., & Murmann, B. (2004). Brief Introduction to Scanning Electron Microscopy (SEM). Http://Cfamm.Ucr.Edu/Documents/Sem-Intro.Pdf, (i), 35–37. https://doi.org/10.12659/MSMBR.893327

Mukhtar, M., Lusitra, M., & Saleh, R. (2012). Co-Precipitation Synthesis and Characterization of Nanocrystalline Zinc Oxide Particles Doped with Cu2+ Ions. Materials Sciences and Applications, 3(August), 543–551. https://doi.org/10.4236/msa.2012.38077

Rosydah, N., Purwaningsih, S. Y., & Darminto. (2009). Sintesis Nanopartikel ZnO dengan Metode Kopresipitasi. Jurnal Teknik POMITS, 7(2), 1–7.

Tawainella, R. D., Riana, Y., Fatayati, R., Kato, T., & Iwata, S. (2014). Sintesis Nanopartikel Manganese Ferrite ( MnFe 2 O 4 ) dengan Metode Kopresipitasi dan Karakterisasi Sifat Kemagnetannya, XVIII(April), 1–7.

Witjaksono, A. (2011). Karakterisasi Nanokristalin Zno Hasil Presipitasi Dengan Perlakuan Pengeringan, Anil Dan Pasca-HidrotermaL. Universitas Indonesia.


Refbacks

  • There are currently no refbacks.