Analysis the rate of metal corrosion using dip-coating electrolyte solutions

Miranda Miranda, Rahmawati Rahmawati

Abstract


This study aims to determine how to test the rate of metal corrosion using dip-coating electrolyte solutions. The electrolyte solutions used are vinegar, lime juice, saltwater, and rainwater—this research conducted by the method of losing weight by dipping the electrolyte solution. The sample immersed for 27 days. The calculation results obtained and samples without coating have a high corrosion rate, so they destroyed quickly. The higher the value of the corrosion rate, the more easily destroyed it will be, and the sample will easily weather/damaged. Likewise, on the contrary, the lower the corrosion rate, the less corrosion that occurs, and the better the sample is protected from rust.

 


Keywords


Corrosion rate; dip-coating; electrolyte solution

Full Text:

PDF

References


Afandi, Y. K., Arief, I. S., & Amiadji. (2015). Analisa Laju Korosi pada Pelat Baja Karbon dengan Variasi Ketebalan Coating. Jurnal Teknik Its, 4(1), 1–5.

Caniago, Z. B. (2006). Kecepatan Korosi Oleh 3 Bahan Oksidan Pada Plat Besi. Jurnal Gradien, 2(2), 161–166.

Djaprie S ., 1995, Ilmu dan Teknologi Bahan , ed. 5, hal. 483-510. Erlangga, Jakarta.

Erna, M., Alif, A., Arief, S., & Jain Noordin, M. (2009). Sintesis dan Aplikasi Karboksimetil Kitosan sebagai Inhibitor Korosi pada Baja Karbon dalam Air. Natur Indonesia, 87(121), 87–92.

Evi Yufita, Desy Fitriana, Zulfalina. Pengendalian Laju Korosi Pada Baja Plat Hitam A36 Dalam Medium Korosif Menggunakan Inhibitor Ekstrak Daun Salam. J. Aceh Phys. Soc., Vol.7, No.2 pp. 67-71, 2018. ISSN online:2355-8229

Irianty, R. S., & Sembiring, M. P. (2012). Pengaruh Konsentrasi Inhibitor Ekstrak Daun Gambir Dengan Pelarut Etanol-Air Terhadap Laju Korosi Besi Pada Air Laut. Jurnal Riset Kimia, 5(2), 165. https://doi.org/10.25077/jrk.v5i2.218

K, S. N., & Misbah, M. N. (2012). Analisis Pengaruh Salinitas dan Suhu Air Laut Terhadap Laju Korosi Baja A36 Pada Pengelasan SMAW. Jurnal Teknik ITS, 1, G75–G77.

Kirk-Othmer. (1965). Encyclopedia of Chemical Technology. 1(5th Edition). Retrieved from http://books.google.com.br/books?id=ziawsTEKsYEC

Lusiana Br Turnip, Sri Handani, Sri Mlyadi. 2015. Pengaruh Penambahan Inhibitor Ekstrak Kulit Buah Manggis Terhadap Penurunan Laju Korosi Baja ST-37. Jurnal fisika unnand vol. 4,. No.2

Nasution, M. (2018). Karakteristik Baja Karbon Terkorosi. 14(1).

Nugroho, F. (2015). Penggunaan inhibitor untuk meningkatkan ketahanan korosi pada baja karbon rendah. Angkasa, VII(1), 151–158.

Setyawan, D. H., Risanti, D. D., & Mawarani, L. J. (2014). pencegahan korosi dengan menggunakan inhibitor natrium silikat(na 2 sio 3 ) hasil sintesis dari lumpur lapindo pada baja tulangan beton. Institut Teknologi Sepuluh Nopember (ITS), 1–6.

Sari, D. M., Handani, S., Yetri, Y., Fisika, J., Mipa, F., & Andalas, U. (2013). pengendalian laju korosi baja st-37 dalam medium asam klorida dan natrium klorida menggunakan inhibitor ekstrak daun teh (Camelia sinensis). Fisika Unand, 2(3), 204–211.

Susetyo, F. budhi, Qadri, M., Maghfurah, F., & Yulianto, S. (2013). analisis kinerja pelat besi berkarat oleh rust remover x. Spektrum Industri, 11(2), 117–242.

Trethewey, K.R. and J. Chamberlain. Korosi Untuk Mahasiswa dan Rekayasawan, Gramedia Pustaka Utama, Jakarta, (1991).

Varde, N., & Fogler, H. S. (1992). Elements Of Chemical Reaction Engineering. In Chemical Engineering Education (Vol. 35).

Yunaidi. (2016). Perbandingan Laju Korosi Pada Baja Karbon Rendah dan Stainless Steel Seri 201 , 304 , dan 430 Dalam Media Nira. Mekanika Dan Sistem Termal (JMST), 1(April), 1–6.

Yudha Kurniawan Afandi, Irfan Syarif Arief, dan Amiadji. 2015. Analisa Laju Korosi pada Pelat Baja Karbon dengan Variasi Ketebalan Coating. JURNAL TEKNIK ITS Vol. 4, No. 1 ISSN 2337-3539 (2301-9271 Printed)




DOI: http://dx.doi.org/10.30870/gravity.v6i2.6830

Refbacks

  • There are currently no refbacks.


Gravity has been indexed by:

     
     

 

  

 

Gravity : Jurnal Ilmiah Penelitian dan Pembelajaran Fisika is publihed by Department of Physics Education, Universitas Sultan Ageng Tirtayasa jointly with Physical Society of Indonesia (PSI)

Creative Commons License 

Gravity : Jurnal Ilmiah Penelitian dan Pembelajaran Fisika is licensed under a Creative Commons Attribution-ShareAlike 4.0 International License

Copyright © 2020, Gravity: Jurnal Ilmiah Penelitian dan Pembelajaran Fisika.